MRC | Criteria | Characteristic |
---|
AARN | FABRICATION METHOD | EXTRUDED" |
ABKW | OVERALL HEIGHT | 1.238 INCHES MINIMUM AND 1.262 INCHES MAXIMUM" |
ABMK | OVERALL WIDTH | 1.238 INCHES MINIMUM AND 1.262 INCHES MAXIMUM" |
ABRY | LENGTH | 10.000 FEET MINIMUM AND 12.000 FEET MAXIMUM" |
ADXL | LEFT SIDE FLANGE THICKNESS | 0.242 INCHES MINIMUM AND 0.258 INCHES MAXIMUM" |
AGTA | BASIC SHAPE STYLE | ANGLE" |
AJGL | FILLET RADIUS WHERE LEFT FLANGE JOINS BASE FLANGE | 0.172 INCHES MINIMUM AND 0.204 INCHES MAXIMUM" |
AJGP | BASE FLANGE THICKNESS | 0.242 INCHES MINIMUM AND 0.258 INCHES MAXIMUM" |
AJJB | FIRST TIP RADIUS | 0.109 INCHES MINIMUM AND 0.141 INCHES MAXIMUM" |
BRFD | WEIGHT PER UNIT MEASURE | 0.683 POUNDS PER LINEAR FOOT" |
CMZY | FIRST TIP STYLE | RIGHT QUARTER RADIUS" |
CMZZ | SECOND TIP RADIUS | 0.109 INCHES MINIMUM AND 0.141 INCHES MAXIMUM" |
CNQJ | SECOND TIP RELATIONSHIP TO FIRST TIP | NOT IDENTICAL" |
CNQK | SECOND TIP STYLE | UPPER RADIUS" |
CQHP | LEFT INSIDE ANGLE | 90.0 DEGREES NOMINAL" |
HEAT | HEAT TREATMENT | T-6511 SOLUTION HEAT TREATED AND STRESS RELIEVED BY STRETCHING" |
MATL | MATERIAL | ALUMINUM ALLOY AMS-QQ-A-200/11, ALLOY 7075" |
ZZZT | NONDEFINITIVE SPEC/STD DATA | ALLOY 7075, TEMPER T6511" |
AARN | FABRICATION METHOD | EXTRUDED" |
ABKW | OVERALL HEIGHT | 1.238 INCHES MINIMUM AND 1.262 INCHES MAXIMUM" |
ABMK | OVERALL WIDTH | 1.238 INCHES MINIMUM AND 1.262 INCHES MAXIMUM" |
ABRY | LENGTH | 10.000 FEET MINIMUM AND 12.000 FEET MAXIMUM" |
ADXL | LEFT SIDE FLANGE THICKNESS | 0.242 INCHES MINIMUM AND 0.258 INCHES MAXIMUM" |
AGTA | BASIC SHAPE STYLE | ANGLE" |
AJGL | FILLET RADIUS WHERE LEFT FLANGE JOINS BASE FLANGE | 0.172 INCHES MINIMUM AND 0.204 INCHES MAXIMUM" |
AJGP | BASE FLANGE THICKNESS | 0.242 INCHES MINIMUM AND 0.258 INCHES MAXIMUM" |
AJJB | FIRST TIP RADIUS | 0.109 INCHES MINIMUM AND 0.141 INCHES MAXIMUM" |
BRFD | WEIGHT PER UNIT MEASURE | 0.683 POUNDS PER LINEAR FOOT" |
CMZY | FIRST TIP STYLE | RIGHT QUARTER RADIUS" |
CMZZ | SECOND TIP RADIUS | 0.109 INCHES MINIMUM AND 0.141 INCHES MAXIMUM" |
CNQJ | SECOND TIP RELATIONSHIP TO FIRST TIP | NOT IDENTICAL" |
CNQK | SECOND TIP STYLE | UPPER RADIUS" |
CQHP | LEFT INSIDE ANGLE | 90.0 DEGREES NOMINAL" |
HEAT | HEAT TREATMENT | T-6511 SOLUTION HEAT TREATED AND STRESS RELIEVED BY STRETCHING" |
MATL | MATERIAL | ALUMINUM ALLOY AMS-QQ-A-200/11, ALLOY 7075" |
ZZZT | NONDEFINITIVE SPEC/STD DATA | ALLOY 7075, TEMPER T6511" |